国产精品国产自产 I 96亚洲精品久久久蜜桃 I 涩视频在线 I 翔田千里精品久久一区二 I 337p日本欧洲亚洲大胆 I 字幕日韩视频一区二区 I 日韩偷拍一区二区 I 免费一级大片 I 九九久久精品国产av片国产 I 午夜福利92国语 I 国产免费97 I 波多野结衣福利视频 I 男人和女人在羞羞视频 I 久久精彩视频 I 忘忧草社区中文字幕www I 日韩影视一区二区三区 I 青青av I 国产av熟女一区二区三区 I 亚洲日韩片无码中文字幕 I 懂色av一区二区三区四区 I 国产伦人人人人人人性 I 91亚洲黄色 I 人妻丰满熟妇av无码区免 I 中文字幕人成人乱码亚洲电影 I 大伊人久久 I 免费人成在线观看网站品爱网 I 黄色三级免费片 I 我看午夜视频 I 性欧美色图 I 日韩三级一区二区

      Rubber products differ from other engineering materials in that the processing process of rubber products usually faces many unique problems which are different from the common problems of other non-rubber materials in the processing process. So today we talk in detail about some of the main problems existing in the production process of rubber products, which may lead to problems and solutions!

1. Rubber products are too rough

Cause analysis: 

1. The mold surface is rough and not cleaned

2. The coke burning time of mixing glue is too short.

    Solution: clean the mold; Prolong the burning time.

2, rubber products rubber edge is too thick, the product is overweight

Cause analysis: 

1. Too much plastic material in the mold

2. Insufficient plate pressure

3. There is no corresponding residual groove in the mold.

Solution: 

1. Strictly control the unit consumption of semi-finished products

2. Increase plate pressure

3. Improve mold design.

3, rubber products have bubbles

Cause analysis: 

1. There are impurities or oil stains in the mold or rubber material.

2. Insufficient curing.

3. Not enough stress.

4. Vulcanized mold temperature is too high.

5 curing agent added less, curing speed is too slow.

Solutions: 1. Pressure

 2. Lengthen the sulfur 

3. Adjust the formula, speed up the vulcanization.

4. Exhaust more. 

5. The mode temperature cannot be too high. 

6. Increase the dosage of vulcanizing agent.

4, rubber products tear

Reason analysis: 

1. Vulcanization speed is too fast, the glue flow is not sufficient. 

2. The mold is dirty or the glue is sticky.

3. Too much isolator or release agent. 

Solution: 

1.Reduce the mold temperature and slow down the vulcanization speed.

2.Keep the glue. Mold cleaning.

3. Use less isolation agent or release agent. 

4. The glue is thick enough.

5, rubber products lack of glue

Cause analysis: 

1. The rubber material does not flow fully;

2. Insufficient single consumption of semi-finished products or insufficient glue loading;

3.  Poor exhaust performance of the die; Mold temperature is too high

Solution: 

1. Slow down the mold rising speed and repeatedly deflate;

2. Reformulate the mold filling amount;

3. Improve mold design and reduce mold temperature.